Taylor dispersion analysis (TDA) is a powerful sizing technique very well suited for (macro)molecules between angstroms and submicrons (typically up to 200 nm). However, new detection modes are required for non-UV-absorbing (macro)molecules such as most of the polysaccharides, including starches. In this work, two different detection modes were compared, backscattering interferometry (BSI) and UV-photooxidation detection (UV-POD). TDA-BSI measures the relative change of the refractive index between eluent and sample (water as eluent in this work), whereas TDA-UV-POD detects the UV-absorbing photo-oxidized products of polysaccharides/starches in strong alkaline media (130 mM NaOH or 1 M KOH). TDA-UV-POD detection was evaluated for linearity and sensitivity at two wavelengths, 214 and 266 nm. The mass-average hydrodynamic radius (Rh) obtained by TDA-BSI and TDA-UV-POD was found to be in excellent agreement, whereas higher average Rh values were obtained by batch dynamic light scattering (DLS) under the same conditions, because of the higher sensitivity of DLS to large-size solutes and aggregates. The hydrodynamic radius distributions obtained by TDA and DLS are intrinsically different but both techniques were found to be complementary, providing useful information on sample dispersity. Owing to the absence of the stationary phase, low sample consumption with straightforward sample preparation (no filtration), and no calibration, TDA is anticipated to become a method of choice for the size-based characterization of polysaccharides, including starches.

Separation efficiency is ideally controlled by molecular diffusion in capillary electrophoresis (CE). However, other adverse phenomena, such as solute adsorption on capillary surface, tend to increase the peak dispersion. An interesting alternative to limit the solute adsorption is to avoid as much as possible the contact of the solute with the capillary surface by elaborating superhydrophobic (SH) coatings on fused silica capillary surfaces. This work describes an optimized protocol to get non-wettable SH coating using hydrophobically modified silica nanoparticle suspensions (Glaco TM), based on simple capillary flushes and thermal stabilization. In this protocol, the control of the air flushing after the introduction of the Glaco TM suspension in the capillary was found crucial to get optimized coating coverage and reproducibility. The SH coating was characterized by ellipsometry, atomic force microscopy, scanning electron microscopy, contact angle (about 159°) and the observation of the meniscus of water in the coated capillary. The hydrodynamic behavior of the SH coated capillary was investigated by plotting the Poiseuille law. Finally, electrophoretic separations of a peptide mixture in acidic conditions demonstrated the interest of this approach with an increase by a factor 2 of the separation efficiency compared to fused silica capillary.

Nanofilms of thickness of about two nanometers have been formed at the air-water interface using functionalized castor oil (ICO) with cross-linkable silylated groups. These hybrid films represent excellent candidates for replacing conventional polymeric materials in biomedical applications, but they need to be optimized in terms of biocompatibility which is highly related to protein adsorption. Neutron reflectivity has been used to study the adsorption of two model proteins, bovine serum albumin and lysozyme, at the silylated oil (ICO)-water interface in the absence and presence of salt at physiologic ionic strength and pH and at different protein concentrations. These measurements are compared to adsorption at the air-water interface. While salt enhances adsorption by a similar degree at the air-water and the oil-water interface, the impact of the oil film is significant, with adsorption at the oil-water interface three-to four-fold higher compared to the air-water interface. Under these conditions, the concentration profiles of the adsorbed layers for both proteins indicate multilayer adsorption: The thickness of the outer layer (oil-side) is close to the dimension of the minor axis of the protein molecule, ~ 30 Å, suggesting a side-way orientation with the long axis parallel to the interface. The inner layer extends to 55-60 Å. Interestingly, in all cases, the composition of oil film remains intact without significant protein penetration into the film. The optimal adsorption on these nanofilms, 1.7-2.0 mg•m-2 , is comparable to the results obtained recently on thick solid cross-linked films using quartz crystal microbalance and atomic force microscopy, showing in particular that adsorption at these ICO film interfaces under standard physiological conditions is non-specific. These results furnish useful information towards the elaboration of vegetable oil-based nanofilms, in direct nanoscale applications or as precursor films in the fabrication of thicker macroscopic films for biomedical applications. 2

The mechanical properties of soft matter are of great importance in countless applications, in addition of being an active field of academic research. Given the relative ease with which soft materials can be deformed, their non-linear behavior is of particular relevance. Large loads eventually result in material failure. In this Perspective article, we discuss recent work aiming at detecting precursors of failure by scrutinizing the microscopic structure and dynamics of soft systems under various conditions of loading. In particular, we show that the microscopic dynamics is a powerful indicator of the ultimate fate of soft materials, capable of unveiling precursors of failure up to thousands of seconds before any macroscopic sign of weakening.

The hysteretic softening at small dynamic strains (Payne effect) related to the rolling resistance and viscoelastic losses of tires was studied as a function of particle size, filler volume fraction, and temperature for carbon black (CB) reinforced uncrosslinked styrene-butadiene rubber (SBR) and a paste-like material composed of CB-filled paraffin oil. The low strain limit for dynamic storage modulus was found to be remarkably similar for CB-filled oil compared to CB-filled SBR. Small-angle X-ray scattering (SAXS) measurements on the simple composites and detailed data analysis confirmed that the aggregate structures and nature of filler branching/networking of carbon black were virtually identical within oil compared to the high molecular weight polymer matrix. The combined dynamic rheology and SAXS results provide clear evidence that the deformation-induced breaking (unjamming) of the filler network – characterized by filler-filler contacts that are percolated throughout the material – is the main cause for the Payne effect. However, the polymer matrix does play a secondary role as demonstrated by a reduction in Payne effect magnitude with increasing temperature for the CB-reinforced rubber, which was not observed to a significant extent for the oil-CB system.

We report the measurement of the interaction energy between a charged Brownian polystyrene particle and an air–water interface. The interaction potential is obtained from the Boltzmann equation by tracking particle interface distance with a specifically designed Dual-Wave Reflection Interference Microscopy (DW-RIM) setup. The particle has two equilibrium positions located at few hundreds of nanometers from the interface. The farthest position is well accounted by a DLVO model complemented by gravity. The closest one, not predicted by current models, more frequently appears in water solutions at relatively high ions concentrations, when electrostatic interaction is screened out. It is accompanied by a frozen rotational diffusion dynamics that suggests an interacting potential dependent on particle orientation and stresses the decisive role played by particle surface heterogeneities. Building up on both such experimental results, the important role of air nanobubbles pinned on the particle interface is discussed.